Evolution Lite is a reduced-gold ceramic alloy, suitable for conventional metal-ceramics. The higher strength imparts this alloy with a high marginal strength, in particular during multiple firing, and allows accurately fitting restorations to be produced.
Indications*
- Onlays, ¾ crowns, crowns
- Telescope crowns, conus crowns
- Bridges
- Wide-span bridges
- Cast posts / cores, bars, attachments
- Implant-supported superstructures
- Partial dentures
Technical Data
| Composition (%): | Au 40.3 | Pd 39.3 | Ag 9.2 | In 9.3 | Ga 1.8 | Ru <1.0 |
| ISO | 22674:2016 |
| ADA Class: | High Noble |
| Type / Color: | 4 / White |
| Density (g/cm³) | 12.8 |
| Melting Range (Solidus/Liquidus): | 1100 - 1260 °C |
| Elastic Modulus (GPa): | 130 |
| Porcelain Fired Hardened | |
| Vickers Hardness: | 280 295 |
| Tensile Strength (MPa): | 790 795 |
| 0.2% Proof Stress (MPa): | 565 650 |
| Elongation (%): | 12 10 |
Advantages
- Light oxide
- Good melting and flow properties
- High resistance to marginal deformation with multiple firings
- Compatible with metal-ceramics (e.g. IPS Style)
- Tested biocompatibility
Processing Data
| Investment Material: | Phosphate-bonded |
| Preheating / Burn- out Temperature: | 750 - 820 °C |
| Crucible | Ceramic crucible |
| Casting Temperature: | 1315 - 1375 °C |
| Oxidation °C/min/Vacuum: | 950 / 5 / No |
| CTE: | (25 – 500 °C): 14.2 x 10-6 /K |
| Recommended Metal Ceramic: | IPS Style, IPS InLine One, IPS InLine, IPS Classic |
| Laser Welding Wire: | Laser Ceramic White |
*See TYPE CLASSIFICATION DUE TO PHYSICAL PROPERTIES