Evolution Lite is a reduced-gold ceramic alloy, suitable for conventional metal-ceramics. The higher strength imparts this alloy with a high marginal strength, in particular during multiple firing, and allows accurately fitting restorations to be produced. Onlays, ¾ crowns, crowns Telescope crowns, conus crowns Bridges Wide-span bridges Cast posts/ cores, bars, attachments Implant-supported superstructures Partial Dentures Light oxide Good melting and flow properties High resistance to marginal deformation with multiple firings Compatible with metal-ceramics (e.g. IPS Style) Certified biocompatibility
Indications*
Advantages
| Composition (%): | Au 40.3 | Pd 39.3 | Ag 9.2 | In 9.3 | Ga 1.8 | Ru < 1.0 | |
| ISO | 22674 : 2016 | |
| ADA Class | High Noble | |
| Type / Color | 4 / White | |
| Density (g/cm3): | 12.8 | |
| Melting Range ( Solidus / Liquidus): | 1100 - 1260 C | |
| Elastic Modulus (GPa): | 130 | |
| . | Porcelain Fired | Hardened |
| Vickers Hardness: | 280 | 295 |
| Tensile Strength (MPa): | 790 | 795 |
| 0.2% Proof Stress (MPa): | 565 | 650 |
| Elongation (%): | 12 | 10 |
| Investment Material: | Phosphate - bonded | |
| Preheating / Burn-out Temperature: | 750 - 820 C | |
| Crucible | Ceramic crucible | |
| Casting Temperature | 1315 - 1375 C | |
| Oxidation C / min / Vacuum: | 950 / 5 / No | |
| CTE: | (25 - 500 C): 14.2 x 10-6 / K | |
| Recommending Metal Ceramic: | IPS Style, IPS InLine One, IPS InLine, IPS Classic, IPS d. SIGN | |
| Laser Welding Wire: | Laser Ceramic White | |